水性木器漆用乳液THYOSIL E1549

Description描述
THYOSIL E1549 is an acrylic emulsion polymer designed for manufacturing primers and topcoats for interior wood. It provides good early sandability after short drying.
是一款丙烯酸乳液聚合物,為家具或室內(nèi)木器底漆和面漆所設(shè)計(jì)。提供好的打磨性和快干性能。
Characteristics特性
Recommended as a sealer. It gives excellent clarity when is applied on both dark and light woods.
具有清晰通透的質(zhì)感,可以適于明或暗的木材。
The excellent selfcrosslinking chemistry is responsible for its fast curing time, good stain and block resistance. 優(yōu)異的自交聯(lián)化學(xué)特性,支持快速固化,抗沾污抗龜裂。
Advantages優(yōu)勢(shì)
ü Excellent resistance to household chemicals優(yōu)異的抗家用(日用)化學(xué)腐蝕性
ü Very good adhesion非常好的附著力
ü Low water absorption 低吸水性
ü Highly sandability 高打磨性
Compatibility配伍性
THYOSIL E1549 is compatible with emulsions and resins manufactured by DIRANSA.
可以與DIRANSA 產(chǎn)的相關(guān)樹(shù)脂和乳液相配
Typical Properties典型值
These properties are typical, do not constitute specifications
Appearance外觀 | Light yellow opaque liquid淡黃色不透明液體 |
Solids (%) 固含量 | 40 |
pH | 8.0 |
Viscosity a 25oC (cP)粘度 | < 100 |
MFFT (oC)成膜溫度 | 53 |
Particle size (nm)粒徑 | 110納米 |
Dried film干膜 | Clear without residual tack成膜干后清晰不回粘 |
Starting Formulation基礎(chǔ)配方(底漆)
Sealer 普通木材 | Sealer for wood with high tannin content 單寧含量高的木材 | |
Raw material原料 | (%) | (%) |
THYOSIL E1549 | 40,0 | 75,0 |
Water水 | 50.9 | 8.0 |
Dowanol DPM (1)二丙二醇單甲醚 | 6.0 | 11.4 |
Butyl Glycol 丁基乙二醇 | 3.0 | 5.4 |
BYK 024 (2) 消泡劑 | 0.1 | 0.2 |
Total | 100,00 | 100,00 |
1: Dow; 2: Byk Chemie
Typical properties: 典型特性(底漆)
Test測(cè)試 | Sealer 普通木材 | Sealer for wood with high tannin content 單寧含量高的木材 |
Solid content 固含量 | 16% | 30% |
Viscosity Cup Ford N°4 at 25°C 粘度4號(hào)福特杯 | 10 sec秒 | 20 sec秒 |
pH | 7.5 | 8.0 |
Application應(yīng)用
· A smooth surface is obtained by sand the wood with #150-320 grit sandpaper.
· 用# 150 - 320砂紙把木頭的表面打磨光滑。
· After applying a first coating, wait until it gets dried. Then sand the applied wood using #320 grit sandpaper.
· 油完第一層后,等到它變干。然后再使用# 320砂紙打磨。
· A second coat is applied and the wood is left for two weeks driying before performing the quality tests.
· 油完第二層后,放置2周后測(cè)試其品質(zhì)性能。
Test測(cè)試 | Result結(jié)果 |
Film appearance 成膜外觀 | Good好 |
Gloss 亮度 | Good好 |
Adhesion 附著力 | Excellent非常好 |
Water proof 耐水性 | Excellent非常好 |
Ethanol 50% resistance 抗50%的乙醇 | Excellent非常好 |
Block resistance 抗結(jié)塊 | Excellent非常好 |
Formulation Tips 配方提示
?Coalescent(成膜助劑): THYOSIL E1549 could be used at normal temperatures with the addition of coalescing solvents. The selection of an optimum coalescing system depends on the required drying rate, temperature and relative humidity. It is usually recommended 30% of coalescing solvents but it may be used lower levels depending on the porosity of the substrate, the type of application equipment, moisture conditions and co-solvents used in the formulation. Reducing the amount of coalescent allows faster drying but an excessive reduction may result in poorer film formation and consequently the loss of the stain resistance. Various types of coalescing may be used. It must be determined for each application.
It is recommended to allow the formulations equilibrating for at least 8 hours after addition of coalescing agents to obtain consistency results in the tests performed.
THYOSIL E1549 可以在常溫下可以與溶劑混合,根據(jù)所需要的干燥速度,溫度和濕度,選擇最佳的配比??梢栽诔叵驴梢蕴砑映赡ぶ鷦?,根據(jù)所需要的干燥速度,溫度和濕度,選擇最佳的配比。通常推薦使用 30%的成膜助劑(與配方中E1549的固含量相比),也可以低于或高于此水平,取決于基材的具體特性,所使用的設(shè)備,水分含量等條件。減少成膜助劑的使用干燥速度會(huì)快,但若添加太少會(huì)影響成膜性,同時(shí)還會(huì)減少防污性能??梢允褂酶鞣N成膜助劑,它必須適合所需要的應(yīng)用,添加的成膜助劑要8小時(shí)前后測(cè)試結(jié)果沒(méi)有變化。
?Rheology Modifiers: 流變改性劑We suggest the use of associative thickeners. Keep in mind that the efficiency of urethane associative thickeners depends largely on the selection of coalescing adopted
我們推薦使用締合型增稠劑,記住聚氨酯締合增稠劑的效果取決于成膜助劑的選擇。
?Antifoam:消泡劑Antifoam should be tested in each case. Care must be taken with the concentration chosen as an excess of antifoaming can cause fish eyes defects or loss of transparency of the film.